high conductivity CCA (Copper Clad Aluminum wire)

high conductivity CCA (Copper Clad Aluminum wire)
Product Detailed
It has become the most common wire used in CATV and other high-frequency conduct cable.

CCA wire

1) Diameter: 0.10 - 2.00mm2) It is divided into annealed state (A kind) and hard state (H kind) 3) It is divided into 10% and 15% two kinds according to volume scale of copperlayer4) The DC resistivity at temperature of 20°C is less than 0.02676Ω.mm²/m5) Its nominal density is 3.32g/cm³ - 3.63g/cm³, it is 35 - 37%of pure copper wire6) Under the same weight, its length is 2.5 - 2.7 times that of pure copper wire7) It has become the most common wire used in CATV and other high-frequency conductcable8) It is a bimetallic wire with a copper cladding concentrically covering an aluminumcore, integrating the beneficial properties of the wonderful conductivity ofcopper and the light-weight of aluminum9) It can be scientifically processed into bare wire and flat wire, and it is thebest material for coaxial cable, computer cable, telephone cable and shieldingcable10) The processing method is similar to that of copper wire during cable manufacturePacking: Plastic/ metal reel & paper carton & wooden pallet.

         Product Specification of CCA

Conductivity coefficient           0.02616

Electrical Conductivity                 66%

Tensile strength                       120Mpa

Elongation                                ≥12%

Density                         3.32g/cm3 – 3.63g/cm3

Range                              0.12mm – 2.05mm

high conductivity CCA (Copper Clad Aluminum wire)